Hi Temp 150.
[Runs on Figure 4 DLP]
HighTemp Flame Retardant
Save on Tooling Costs and Time with Direct Production of Flame-Resistant Plastic Parts
Figure 4 High Temp 150°C FR Black is a rigid, flame-retardant black material that can be used for production parts requiring UL94 V0 rating as well as FAR 25.853 and 23.853 capability. It provides long-term environmental stability with an injection molded-like surface quality.
This material is recommended for consumer, transportation, and aerospace applications that require performance at high temperatures like brackets, covers, and circuit board housings and covers.
Figure 4 High Temp 150°C FR Black is tested to 8 years of indoor and 1.5 years outdoor mechanical performance per ASTM D4329 and ASTM G194 methods, ensuring that printed parts remain functional and stable for long periods in real-world conditions.
Applications
Printed circuit board covers
Electrical and under-hood housings requiring UL94 V0 rating
Rigid covers, hangers, and brackets
Small FAR 25/23.853 in-cabin parts
Flame retardant parts for trains and buses
Benefits
Self-extinguishing, flame-retardant material
Halogen-free
High heat deflection temperature for demanding applications
No secondary thermal cure required
Excellent surface quality, accuracy & repeatability
Capable of plating and painting
DOwnload data sheet >>>>
Features
Passes UL94 V0 test standards @ 2 mm and 3 mm thickness
Passes FAR Part 25.853 @ 12-second vertical burn and HB testing @ 3 mm thickness
Passes FAR Part 23.853 @ 12-second vertical burn and HB testing @ 3 mm thickness
Passes UL 746C GWIT and GWFI @ 2 mm and 3 mm thickness
>150C @ 0.455 MPa HDT
2900 MPa flexural modulus
Long-term indoor and outdoor environmental stability of mechanical properties; tested out to 8 and 1.5 years (respectively) per ASTM methods
READY TO print WITH
hi temp 150?
Need rigid DLP parts that maintain performance at elevated temperatures? Upload your model for a quote or speak with our team about thermal requirements, quantities, tolerances and finishing.